TEKNOBRITE
CZ 920 BRIGHTENER |
TEKNOBRITE AZ 846 A
TEKNOBRITE AZ 846 B
TEKNOBRITE AZ 1045 COM
TEKNOBRITE AZ 1045 COR
TEKNOBRITE AZ 1045 COL
PH
Temperature
Current density |
130 – 150 g/l
250 g/l
40 – 60 ml/l
0.1 – 0.4 ml/l
10 – 20 ml/l
5.0 – 5.4
21 – 35 ºC
1.2 – 2.5 A/dm2 |
A unique cobalt-zinc alloy plating process which gives
two to three time better corrosion resistance than available from
zinc deposits of equal thickness.
Exceptionally bright deposits & can be used for both vat &
barrel applications.
Produces high quality deposits and meets international specifications. |
TEKNOBRITE
ZR – 105
ZINC-IRON ALLOY PLATING PROCESS |
Zinc as metal
Sodium Hydroxide
TEKNOBRITE ZR – 105 STARTER
TEKNOBRITE ZR – 105 SOLUBILIZER
TEKNOBRITE ZR – 105 A
TEKNOBRITE ZR – 105 B
TEKNOBRITE ZR – 105 C
Temperature
Current density
- Rack
- Barrel
Voltage
- Rack
- Barrel |
8 – 18 g/l
75 – 160 g/l
8 – 12 ml/l
35 – 50 g/l
10 – 15 ml/l
0.1 – 0.2 ml/l
0.8 – 1.5 ml/l
20 – 30 ºC
1.0 – 3.0 A/dm2
0.5 – 1.5 A/dm2
3 – 6 V
8 – 16 V |
Uniform bright deposit over a wide current density range.
Good corrosion & abrasion resistance.
Deposits accepts silver free black chromate as well as conventional
bronze iridescent and clear chromate conversion.
Uniform distribution of metal. |
TEKNOBRITE ZINIK
15 ZINC – NICKEL ALLOY PLATING PROCESS
_________________ |
TEKNOBRITE ZINIK BASE A
TEKNOBRITE ZINIK BASE B
TEKNOBRITE ZINIK BRIGHTNER
TEKNOBRITE ZINIK CARRIER ADDITIVE
TEKNOBRITE ZINIK ADDITIVE
Temperature
Current density
- Rack
- Barrel
Voltage
- Rack
- Barrel
________________________ |
100 – 140 ml/l
1.6 – 2.4 ml/l
10 – 15 ml/l
1.2 – 2.0 ml/l
0 – 2 ml/l
20 – 27 ºC
1.0 – 3.0 A/dm2
0.8 – 1.2 A/dm2
12 – 18 V
5 – 10 V
________________ |
A cyanide-free alkaline process, producing bright zinc-nickel
deposits.
The process has excellent throwing power and metal distribution
suitable for both vat & barrel applications.
Excellent corrosion resistance. |