SILVER PLATING PROCESS

Back to products

ARGOMAX BRIGHT SILVER	ARGOMAX BRIGHT SILVER SALT ARGOMAX CARRIER ADDITIVE ARGOMAX BRIGHTENER Current density Temperature	200 g/l 10 – 15 ml/l 20 – 40 ml/l 1 – 2 A/dm2 20 – 30 ºC	High performance bright silver bath based on fully organic addition agent system to produce bright silver deposit on a wide current density range. Mainly used for electrical (Switch Gear) and electronic components.
ARGOASTRA BRIGHT SILVER	ARGOASTRA BRIGHT SILVER SALT ARGOASTRA CARRIER ADDITIVE ARGOASTRA BRIGHTENER Current density Temperature	250 g/l 10 – 15 ml/l 40 – 60 ml/l 1 – 2 A/dm2 20 – 30 ºC	Bright silver system based on fully organic addition agents to produce mirror bright silver deposits having a pleasing white colour and good antitarnishing properties. Designed for plating silver jewellery articles, table ware, cutlery, etc. Silver on silver applications.
ARGOTEK HIGH SPEED SILVER	ARGOTEK BRIGHT SILVER SALT ARGOTEK CARRIER ADDITIVE ARGOTEK BRIGHTENER Current density Temperature	300 g/l 10 – 15 ml/l 30 – 50 ml/l 1.0 – 2.5 A/dm2 20 – 32 ºC	Designed for continuous plating of wire, strips, etc. Can deposit 5 microns per minute at 10 A/dm2.
KEMPAS AG - 107	KEMPAS AG – 107 Time pH Currrent density	250 ml/l 2 – 3mins. 8 – 9 1 – 2 A/dm2	To provide antitarnish coating on silver and gold plated components by giving cathodic current.
KEMPAS AG – 300	KEMPAS AG – 300 Temperature Time	4 – 8 g/l 40 – 45 ºC 4 – 5 mins.	A solvent free emulsion antitarnish for silver deposit. Does not contain halogenated Hydrocarbon solvents.
KEMPAS AG – 208 ____________	KEMPAS AG – 208 Temperature Time _____________________________	10 – 15 gm/l Room. 30 – 60 secs. ______________	An alternate antitarnish i.e. non-silicated passivation for silver plated parts. Room temperature operated. Immersion process and hence easy to operate. Back to Top