KEMPAS
BL– 15 |
KEMPAS bl – 15
Nitric acid
Time |
4.0 – 6.0 g/l
10 – 15 ml/l
5 – 15 secs. |
Blue Zinc passivation on zinc coatings for better
corrosion resistance. |
KEMPAS
BL – 200 |
KEMPAS BL – 200
Time |
50 – 80 ml/l
20 – 30 secs. |
A new trivalent chrome passivation process designed to produce
clear blue chromate conversion coating.
Provides high corrosion resistance and the coating withstands 50
– 60 hours salt spray. |
KEMPAS
IR – 752 |
KEMPAS IR – 752
Nitric acid
PH
Time |
15 ml/l
4 ml/l
0.8 – 1.2
10 – 20 secs. |
Produces yellow iridescent chromate layer over zinc plating for
better corrosion resistance.
Suitable for deposits produced from cyanide zinc and chloride zinc. |
KEMPAS
IR– 763 |
KEMPAS IR – 763A
KEMPAS IR – 763B
Nitric acid
Time
pH |
8.0 – 15 ml/l
5 – 8 g/l
2 – 4 ml/l
10 – 25 secs
0.8 – 1.6 |
Produces excellent iridescent chromate conversion coating for
chloride zinc and cobalt zinc alloy deposits.
Stands corrosion resistance of over 200 hrs. in salt spray for cobalt
zinc deposits. |
KEMPAS
OLIVE 862 |
KEMPAS OLIVE 862
Time
pH |
60 – 120 ml/l
30 – 90 secs.
0.8 – 1.2 |
Produces Olive green chromate conversion coatings on chloride
zinc deposits.
Corrosion resistance of over 150 hours in salt spray.
Suitable for use in automatic plating installations. |
KEMPAS OLIVE COMPOSITE |
KEMPAS OLIVE No. 1
KEMPAS OLIVE No. 2
Nitric acid
pH |
60 – 80 ml/l
50 ml/l
2 – 4 ml/l
0.8 – 1.2 |
Produces Olive green chromate conversion coatings on chloride
zinc deposits.
Corrosion resistance of over 150 hours in salt spray. |
KEMPAS
BK – 66 |
KEMPAS bk – 66a
KEMPAS bk – 66b
Distilled water
Time
pH |
80 ml/l
80 ml/l
840 ml/l
60 – 120 secs.
1.2 – 2.5 |
Produces a uniform jet black coating on zinc, zinc die casting
and zinc plate.
Good corrosion and abrasion resistance |
KEMPAS
BK - 67 |
KEMPAS bk – 67a
KEMPAS bk – 67b
Distilled water
Time
pH |
60 – 80 ml/l
80 – 100 ml/l
To make up 1 ltr.
80 – 120 secs.
1.2 – 2.5 |
Economical black chromate conversion process on zinc coating for
glossy black finish.
Good corrosion and abrasion resistance. |
KEMPAS
BK– 69 |
KEMPAS bk – 69a
KEMPAS bk – 69b
Distilled water
Time
Ph |
80 – 120 ml/l
40 – 65 ml/l
To make up 1 ltr.
30 – 90 secs.
0.8 – 1.4 |
Silver-free black chromate process designed to produce black chromate
conversion coating on
Zinc-Cobalt alloy deposits.
Withstands 100 hours salt spray (white rust) and suitable for automatic
plating units. |
KEMPAS
CAD - 753 |
KEMPAS CAD – 753
Temperature |
60 – 120 g/l
25 – 34 ºC |
A cadmium bright dip of the chromate conversion type that produces
a clear, bright, satin free finish without leaching.
Corrosion resistance of over 90 hours in salt spray. |
KEMPAS ZR |
KEMPAS ZR
Distilled water
Temperature
Time
PH |
40 – 60 ml/l
To make up 1 ltr.
15 – 35 ºC
40 – 75 secs.
0.7 – 1.1 |
Easy maintenance.
Produces uniform jet black coating on zinc-iron plating.
Good corrosion and abrasion resistance.
Being silver-free, the product is comparatively economical. |
DUROSEAL 4500
______________ |
DUROSEAL 4500
Temperature
Immersion time
PH value
_______________ |
5% (v/v)
Room to 60°C
5 secs. – 2 mins.
10.5 – 12.0
________________ |
A unique process for improving the corrosion resistance of clear
chromate coating.
Suitable for both vat & barrel operations.
Easy to operate.
No clogging of holes and threads. |