St Kilda Chemicals - Specialists in Metal Finishing, Zinc and Phosphating

Nickel Plating Process

Cupramax ac 582	Copper Sulphate Sulphuric acid CUPRAMAX AC 582 CUPRAMAX AC 583 Chloride Temperature Current density	: 175 – 250 g/l : 25 – 35 ml/l : 4 – 6 ml/l : 0.3 – 0.7 ml/l : 100 – 130 ppm : 20 – 32ºC : 2 – 6 A/dm2	• Specially formulated for decorative plating on metal and plastic parts. • Produces highly exceptional levelled, brilliant, smooth and ductile copper deposits.. • The bath can be operated at wide bath temperature range 20 – 35°C.
Cupramax acm 682/692	Copper Sulphate Sulphuric acid CUPRAMAXAC682/692 CUPRAMAXAC683/693 Chloride Temperature Current density	: 175 – 250 g/l : 25 – 35 ml/l : 6.0 – 10.0 ml/l : 0.4 – 1.2 ml/l : 100 – 130 ppm : 20 – 35ºC : 2 – 6 A/dm2	• Process has wide brightness range, especially at extreme low current density area for plating on zinc diecasting, steel, aluminium, etc. • Has a wide useful operating range, so the solution control is very easy. • The bath can be operated at wide bath temperature range 20 – 35°C. • Good brightness and levelling. • Good bright throwing power.
Cupramax ac 1882	Copper Sulphate Sulphuric acid CUPRAMAX AC 1882 CUPRAMAX AC 1883 Chloride Temperature Current density	: 175 – 250 g/l : 25 – 35 ml/l : 4 – 6 ml/l : 0.3 – 0.5 ml/l : 100 – 130 ppm : 20 – 32ºC	• Provides wide brightness range. • Bath can be operated at wide bath temperature range 20 – 35 OC. • Good bright throwing power. • Suitable for barrel plating.
Cupramax ac 2082	Copper Sulphate Sulphuric acid CUPRAMAX AC 2082 CUPRAMAX AC 2083 Chloride Temperature Current density	: 175 – 250 g/l : 50 – 70 g/l : 4 – 6 ml/l : 0.3 – 0.6 ml/l : 75 - 150ppm : 20 – 30ºC : 2 – 6 A/dm2	• High performance bright acid copper electroplating bath. • Exceptional leveling and bright throwing power. • Highly ductile and extremely bright deposits.
Cupramax ac 2782	Copper Sulphate Sulphuric acid CUPRAMAX AC 2782 CUPRAMAX AC 2783 Chloride Temperature Current density	: 175 – 250 g/l : 50 – 70 g/l : 6.0 – 10.0 ml/l : 0.3 – 0.6 ml/l : 70 – 140 ppm : 20 – 30ºC : 1 – 6 A/dm2	• Shows excellent levelling, coupled with good throwing power. • Give good corrosion resistance. •Highly ductile and extremelybright deposits.
Cupramax ac 2882	Copper Sulphate Sulphuric acid CUPRAMAX AC 2882 CUPRAMAX AC 2883 Chloride Temperature Current density	: 175 – 250 g/l : 50 – 70 g/l : 4.0 – 6.0 ml/l : 0.3 – 0.6 ml/l : 70 – 140 ppm : 20 – 30ºC : 1 – 6 A/dm2	• Shows excellent levelling, coupled with good throwing power. • Give good corrosion resistance. • Highly ductile and extremely bright deposits.
Cupramax 8100	Copper Sulphate Sulphuric acid CUPRAMAX AC 8100 Chloride Temperature Anodes Anode current density Filtration	: 250 g/l : 50 – 55 g/l : 12 ml/l : 20 - 80ppm : 25 - 40ºC : Phosphorised : 40 A/ft2 : Continous.	• The single addition agent. • Modified to enable the process to be fullyutilized in the plating of printing cylinders. • Produced deposits of excellent ductility, brightness and hardness. Back to Top